2mm HDPE Geomembrane

1.High Strength, excellent tenacity 2.Anti-aging,anti-acid and alkali

Virginal Material HDPE Liner 

 

Production Description 

 

Polyethylene Liners are a range of environmental protection liners for sealingapplications.

These include HDPE (High Density Polyethylene) LDPE (Low Density Polyethylene)and LLDPE (Linear Low Density Polyethylene). Available in a range of thicknessesand surface textures.

 

Application

 

We have  network of approved installers who can arrange on-site weldingand installation services for landfill, stormwater and effluent ponds.Geomembranes are manufactured using high density polyethylene (HDPE). HDPEis produced in various thicknesses and with smooth or embossedstructured surfaces. The  geomembranes provide a complete seal against even the most toxic substances. It  is typically used in sealing applications for landfill base seals as well as caps, in environmental sealing applications for the protection of groundwater from contamination and in water conveyance structures, canals or ponds.

 

Features 

• Versatile sealing applications possible• Excellent chemical resistance due to selected raw materials• Extreme high elongation during uni-axial and multiaxial deformation• High stress cracking resistance• Very high UV-resistance• Direction independent shear stress transfer with structured surfaces• High interface friction angles with embossed structured surfaces• Slope dependent structured surfaces available for project specific designs• Complete quality control from the resin to the final product

• High Melt Flow Index allows an excellent welding performance• Smooth edges with removable plastic tape for clean welding surface and overlap lines• ISO 9001: 2000 certified

 

ASTM GRI-GM13 Standard Properties:

 

 

No.	Item	Test Value
		0.75mm	1.0 mm	1.25 mm	1.5 mm	2.0 mm	2.5 mm	3.0mm
1	Minimum Density(g/cm³)	0.939
2	Tensile Property
	Strength at yield,N/mm	11	15	18	22	29	37	44
	Strength at break ,N/mm	20	27	33	40	53	67	80
	Elongation at yield,%	12
	Elongation at break,%	700
3	Tear Resistance   N	93	125	156	187	249	311	374
4	Puncture Resistance  N	240	320	400	480	640	800	960
5	Stress Crack Resistance, hrs	300
6	Carbon Black Content, %	2.0-3.0
	Carbon Black Dispersion	1  or  2
7	Standard OTI  Min	100
	High Pressure OTI  Min	400
8	Impact Cold Crack at -70°C	Pass
9	Water vapor permeability (g.cm/cm2 .s.Pa)	≤1.0×10-16
10	Dimensional Stability (%)	±2

 

 

2mm HDPE Geomembrane